Abstract Several anti-proteolytic dentin therapies are being exhaustively studied in an attempt to reduce dentin bond degradation and improve clinical performance and longevity of adhesive restorations. Objectives This study assessed the effect of epigallocatechin-3-gallate (EGCG) on long-term bond strength when incorporated into adhesives. Material and Methods Adhesive systems were formulated with EGCG concentrations of 0 wt%: (no EGCG; control); 0.5 wt% EGCG; 1.0 wt% EGCG, and 1.5 wt% EGCG. Flexural strength (FS), modulus of elasticity (ME), modulus of resilience (MR), compressive strength (CS), degree of conversion (DC), polymerization shrinkage (PS), percentage of water sorption (%WS), percentage of water solubility (%WL) and cytotoxicity properties were tested. Dentin microtensile bond strength (µTBS) was evaluated after 24 h and again after 6 months of water storage. The adhesive interface was analyzed using scanning electron microscopy (SEM). Results No significant differences were found among the groups in terms of FS, ME, MR, CS and PS. EGCG-doped adhesives increased the DC relative to the control group. EGCG concentrations of 1.0 wt% and 0.5 wt% decreased the WS of adhesives. WL decreased in all cases in which EGCG was added to adhesives, regardless of the concentration. EGCG concentrations of 1.0 wt% and 0.5 wt% reduced cytotoxicity. EGCG concentrations of 1.0 wt% and 0.5 wt% preserved µTBS after 6 months of storage, while 1.5 wt% EGCG significantly decreased µTBS. SEM: the integrity of the hybrid layer was maintained in the 0.5 wt% and 1.0 wt% EGCG groups. Conclusion EGCG concentrations of 1.0 wt% and 0.5 wt% showed better biological and mechanical performance, preserved bond strength and adhesive interface, and reduced cytotoxicity.

Abstract Objective: The aim of the study was to evaluate the effects of the capping materials mineral trioxide aggregate (MTA), calcium hydroxide (CH) and BiodentineTM (BD) on stem cells from human exfoliated deciduous teeth (SHED) in vitro. Material and Methods: SHED were cultured for 1 – 7 days in medium conditioned by incubation with MTA, BD or CH (1 mg/mL), and tested for viability (MTT assay) and proliferation (SRB assay). Also, the migration of serum-starved SHED towards conditioned media was assayed in companion plates, with 8 μm-pore-sized membranes, for 24 h. Gene expression of dentin matrix protein-1 (DMP-1) was evaluated by reverse-transcription polymerase chain reaction. Regular culture medium with 10% FBS (without conditioning) and culture medium supplemented with 20% FBS were used as controls. Results: MTA, CH and BD conditioned media maintained cell viability and allowed continuous SHED proliferation, with CH conditioned medium causing the highest positive effect on proliferation at the end of the treatment period (compared with BD and MTA) (p<0.05). In contrast, we observed increased SHED migration towards BD and MTA conditioned media (compared with CH) (p<0.05). A greater amount of DMP-1 gene was expressed in MTA group compared with the other groups from day 7 up to day 21. Conclusion: Our results show that the three capping materials are biocompatible, maintain viability and stimulate proliferation, migration and differentiation in a key dental stem cell population.

O texto alerta para a consciência da relação ética da produção intelectual no que refere a quantidade, qualidade, autoria e publicação. Reafirma a importância da questão ética do gerenciamento de grupos de trabalho e a efetiva participação no desenvolvimento do projeto experimental.

This article stresses the importance of ethical relations involved in intellectual production, particularly as regards quantity, quality, authorship and publication. It reaffirms the importance of ethics while managing workgroups, and the effective participation in the development of experimental projects.